Teflon® PFA 9725
全氟烷氧基
The Chemours Company
產品說明:
For inventory control purposes product name may be followed by an X.
Products labeled PFA TE9725 and PFA TE9725 X are equivalent and all information in this document is applicable to both.
Typical Application
Teflon ™ PFA 9725 is an ideal resin for applications involving compounding and compression molding, as well as extruded tubing and other profiles for hose, electrical insulators, and sleeving; industrial film and products made from film; and injection or blow-molded articles requiring superior electrical, chemical, and thermal properties. Teflon ™ PFA 9725 offers a slightly lower melt flow rate than Teflon ™ PFA TE9724, ultimately providing a higher degree of stress-crack resistance.
Description
Teflon ™ PFA 9725 is a general-purpose fluoroplastic resin available as loosely compacted fluff. It is intended for use in special application processes in consultation with Chemours. Compared with other grades of Teflon ™ PFA, its most unique features are a relatively low flow rate and properties that make it suitable for a variety of processes and demanding end uses, especially compounding and compression molding. Table 1 shows the typical property data for Teflon ™ PFA 9725.
Teflon ® PFA TE9725 is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Teflon ® PFA TE9725 can be used to improve processing rates. Compared with other thermoplastics, Teflon ® PFA TE9725 provides a superior balance and level of end-use properties at high service temperatures. Teflon ® PFA TE9725 combines the processing ease of conventional thermoplastics with many properties similar to those of polytetrafluoroethylene.
Properly processed products made from neat Teflon ® PFA TE9725 resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes and excellent weather resistance.
In a flame situation, products of Teflon ® PFA TE9725 resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and dded at a slow rate with very little smoke.
Teflon ® PFA TE9725 meets the requirements of ASTM D3307, Type II
供貨地區：北美洲、拉丁美洲、歐洲、亞太地區
材料特性：Excellent Weather Resistance、低摩擦系數、低吸濕性、低煙度、良好的電氣性能、良好的熔體強度、良好的柔韌性、流動性低、耐化學良好、耐熱中等、熱穩定良好、韌性良好
材料用途：薄膜、電氣/電子應用領域、管道、管件、混料、型材
外觀形式：Fluff
加工方法：復合、擠出、樹脂傳遞成型、壓縮模塑、注射成型
物料性能：
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 密度/比重 | 2.14 | g/cm³ | ASTM D792 |
| 熔流率（熔體流動速率）(372℃/5.0 kg) | 1.7 | g/10 min | ASTM D3307,ISO 12086 |
| 吸水率(24 hr) | < 0.030 | % | ASTM D570 |
| 硬度 | 額定值 | 單位制 | 測試方法 |
| 肖氏硬度(邵氏 D) | 55 | ASTM D2240,ISO 868 | |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 抗張強度(23℃) | 26.2 | MPa | ASTM D3307,ISO 12086 |
| 伸長率(斷裂,23℃) | 300 | % | ASTM D3307,ISO 12086 |
| 彎曲模量(23℃) | 621 | MPa | ASTM D790,ISO 178 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 熔融溫度 | 305 | ℃ | ASTM D4591 |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 體積電阻率 | 1.0E+18 | ohms·cm | ASTM D257,ISO 1325 |
| 介電強度 | |||
| 0.250 mm,方法A（短時間） | 80 | kV/mm | ASTM D149 |
| 0.250 mm | 80 | kV/mm | IEC 60243-1 |
| 介電常數(1 MHz) | 2.03 | ASTM D150,IEC 60250 | |
| 耗散因數(1 MHz) | < 2.0E-4 | ASTM D150,IEC 60250 | |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級1 | V-0 | UL 94 | |
| 極限氧指數 | > 95 | % | ASTM D2863,ISO 4589-2 |
| 補充信息 | 額定值 | 單位制 | 測試方法 |
| MIT Folding Endurance2(200.0 µm) | 5.0E+5 | Cycles | ASTM D2176 |
| 備注 1These results are based on laboratory tests under controlled conditions and do not reflect performance under actual fire conditions,current rating is a typical theoretical value. 2Depending on fabrication conditions |
|||
扎根于過去。放眼于未來。
Teflon™ PFA 是一種四氟乙烯-全氟烷氧基醚共聚物樹脂，可以提供顆粒狀和粉末狀兩種產品形態。這種氟聚合物樹脂可以改進很多行業（包括化學加工、電子、半導體、制藥和生物技術領域）生產的產品。
Teflon™ PFA 樹脂的特性和優勢
Teflon™ PFA 樹脂可以用傳統的熱熔擠出工藝或注塑、壓塑、滾塑成型、傳遞成型和吹塑工藝進行加工。Teflon™ PFA 樹脂的熔體強度和熱穩定性很高，有利于采用較大的模具孔和高溫涂布工藝，從而提高加工速度。
這種樹脂結合了傳統熱塑性樹脂的易加工優勢和 Teflon™ PTFE（聚四氟乙烯）的出色性能，包括：
? 出色的耐化學腐蝕性
? 卓越的電氣性能
? 高達 260℃ (500°F) 的連續工作溫度
? 強大的耐高溫蠕變性能
? 出色的低溫韌性
? 出色的阻燃性
Teflon™ PFA 產品系列
Teflon™ PFA 產品系列包括各種熔體流動速率 (MFR) 的樹脂等級產品，這些產品適用于各種熱塑成型工藝，包括管和薄膜擠出成型、注塑、傳遞成型、壓塑成型和吹塑成型工藝。還可以提供用作涂層、薄膜或彌散材料的 PFA 產品。
Teflon™ PFA 300 系列
? Teflon™ PFA 300 系列樹脂是通用型 PFA 樹脂，適用于模壓或擠塑等熱塑性成型工藝
Teflon™ PFA 400HP 系列
? 完全氟化的 Teflon™ PFA 400HP 系列樹脂專為滿足化學流體處理行業對高純度和最小萃取量的要求而設計。
? Teflon™ PFA HP 氟聚合物樹脂制成的組件具有出色的耐化學腐蝕性和耐環境應力開裂性。這種樹脂幾乎不受任何化學品和溶劑的影響。
Teflon™ PFA 900HP Plus 系列
? Teflon™ PFA 900HP Plus 氟聚合物樹脂具有與 Teflon™ PFA HP 等級產品一樣出色的耐化學腐蝕性、高純度和防離子污染性能，并且具有更長的抗撓曲壽命和更好的耐化學應力開裂性能。此外，這種樹脂還賦予產品更高透明度和更好的表面光潔度，便于觀察在水處理系統中的雜質并防止微生物在表面積聚。
? 這種樹脂能夠提供更穩定可靠，無雜質污染以及耐含氟表面活性劑等特性，滿足于半導體制造加工過程中日益嚴苛的要求。